1. Iron and steel . profiled plates in rolling direction
   鋼鐵.沿軋制方向成型的鋼板
2. Click on the rolling direction of the arrow adjustments , in order to keep the ball to the opposite wall
   點擊滾動的箭頭調(diào)整方向，要想辦法把球踢到墻的對面。
3. And strengthening contribution of t1 phase is maximal in the rolling direction , minimal in the transverse direction , and midterm in the 45 direction , which means that contribution of t1 phase to anisotropy of alloys is contrary to that of textures
   相在縱向和橫向的強化貢獻最大，而在45方向的強化貢獻最小，即與織構(gòu)的作用一致； t _ 1相的強化貢獻則在縱向最小，在橫向最大，在45方向較大，即與織構(gòu)的作用相反。
4. Zircaloy - 4 sheet , which was cold - worked followed by recrystallization annealing , exhibits longer lcf life in the rolling direction than that in the transverse direction , and the fact that difference in lcf life between both directions becomes larger as the range of plastic strain becomes lower can be attributed to the texture effect , p - solution treatment deteriorates the alloy ' s lcf property because the treatment lowers the average value of alloy ' s schmid factors , and the subsequent annealing - treatment in a - phase range has a impact on the lcf properties , i . e . the subsequent annealing - treatment at 500 ? for 1 . 5h results in better property than that at 750 for 1 . 5h , which comes mainly from the fact that the alloy annealled at 500 for 1 . 5h has lower amount of the precipitate particles than the alloy annealled at 750 for 1 . 5h
   對于冷加工后經(jīng)再結(jié)晶退火處理的zr - 4合金，軋制方向的低周疲勞壽命比橫向要大。隨著_ p的降低，兩個方向的低周疲勞壽命的差別相應(yīng)增加，這是由于合金中存在織構(gòu)的緣故。冷加工后經(jīng)再結(jié)晶退火處理的zr - 4合金在固溶處理后，抗疲勞性能明顯降低，這主要是由于固溶處理降低了合金的schmid因子；固溶處理后在相區(qū)的退火對疲勞性能有影響，即500 1 . 5h退火的抗疲勞性能要優(yōu)于750 1 . 5h退火，這主要與500 1 . 5h退火的合金中沉淀相粒子的數(shù)量較少有關(guān)。
5. While cyclic deformation experiment under constant strain control is performed in 400 , the material shows the continuous hardening until cyclic invalidation . ( 3 ) back stress attained by kwl " s method is used to analyse the bauschinger effect during an incremental step cyclic test and cyclic deformation test under constant strain control , it is shown that back stress increases with increasing plastic strain and the numbers of cycle , and the back stress is uniform , regardless of tension or compression conditions . ( 4 ) as far as recrystallized zircaloy - 4 plate is concerned , the back stress in transverse direction is higher than that in rolling direction due to the higher schmid factor in rolling direction
   對于再結(jié)晶狀態(tài)的zr一4合金板材試樣來說， t方向(橫向)試樣的背應(yīng)力要高于r方向(軋制方向)的背應(yīng)力，原因在于r方向的schmid因子高于t方向的schmid因子; 400下， zr一4合金的背應(yīng)力要明顯低于室溫下的背應(yīng)力;含氫200pg / g的zr一4合金的背應(yīng)力大小與無滲氫的zr一4合金背應(yīng)力相比，無明顯區(qū)別;固溶處理后， zr一4合金的背應(yīng)力大小發(fā)生了變化，在較高塑性應(yīng)變下，背應(yīng)力均高于固溶處理前的背應(yīng)力。